1045 steel usually comes in the black hot-rolled variety; however, it also is occasionally manufactured in the normalized condition. This is steel that has been given a heat treatment, intended to bring many samples under consideration into the same condition. 1045 is known for fairly good strength and impact properties. It has good machinability qualities as well as serviceable welding qualities, whether in the rolled or normalized condition. Machinability is the ability to form the finished steel into a machined part.
1045 steel Chemical Composition
Iron is the main part of 1045 steel. However, it does contain certain other elements within a specified range. The first element is carbon, with a range of 0.43 percent to 0.50 percent. Next is silicone, with a range of 0.10 percent to 0.60 percent. The last alloy is manganese, with an allowable range of 0.60 percent to 0.90 percent. Phosphorus may sometimes be found in this product, to a maximum of 0.04 percent.
1045 steel Hot-rolled Mechanical Properties
The tensile strength of 1045 hot-rolled steel is in the range of 570 MPa (a megapascal, a unit of measure equal to 1,000,000 pascals) to 700 MPa. A pascal is the amount of pressure generated by a mass of about 100g on a square meter under the earth's gravitational pull. Hot-rolled bars have a yield strength of 300MPa to 450MPa. Elongation of hot-rolled steel, based on 2 inches, is 14 to 30 percent. Elongation, a test for the ductility of steel, involves making it longer until it fractures. The steel's hardness on the Brinell Hardness Scale is 170 to 210. Brinell hardness is determined by forcing a hard steel or carbide sphere of a specified diameter under a specified load into the surface of a material and measuring the diameter of the indentation left after the test.